Effect Of Resealing On Microleakage Of Resin Composite Restorations In Relationship To Margin Design And Composite Type
Antonson, Sibel A.
Yazici, A. Ruya
Antonson, Donald E.
Hardigan, Patrick C.
xmlui.mirage2.itemSummaryView.MetaDataShow full item record
Objective: To determine the relationship between margin preparation design and resin-composite type on microleakage with or without re-application of surface-penetrating sealant. Methods: Class-I resin-composite restorations were completed for 128 extracted human molars. Half of the margins were beveled, the other half, butt-joint. Half of each group was restored with Filtek-Supreme (FS), the other half with Esthet-X (EX) using their respective adhesive systems. Margins were etched and sealed with a surface-penetrating sealant, Fortify. The samples were stored in water 24h, and thermocycled (5,000 cycles, 5°C–55°C). Then, samples were abraded using a toothbrush machine (6,000 strokes). Half of the restorations from each sealant group (n=16) were resealed, and the other half had no further treatment. Thermocycling and tooth brushing were repeated. The samples were sealed with nail polish, immersed in methylene-blue for 8h, sectioned, and magnified digital photographs were taken. Three examiners assessed dye penetration. A 2×2×2 multi-layered Chi-Square analysis, using Cochran-Mantel-Haenszel test was conducted for statistical analysis. Results: No difference was observed between sealed and resealed FS and EX restorations with butt-joint margins. In beveled margins, resealing caused significantly less microleakage (P<.01). No differences were found between restorations either sealed or resealed with bevel margins. In butt-joint margins, at the leakage level deeper than 2/3 of the preparation depth, resealed FS showed less microleakage than EX resealed restorations (P<.01). Conclusion: Resealing reduced microleakage in bevel margins, however, in butt-joint margins resealing did not affect the leakage. A significant statistical relationship exists between and within resealing, margin preparation design, type of composite, and microleakage.